| UHMW-PE | Economic | Standard | High Performance |
| Density GB/T1033.1-2008 |
0.94 g/cm3 | 0.938 g/cm3 | 0.928 g/cm3 |
| Tensile strength GB/T1040-2006 |
43.6 MPa | 42.6 MPa | 39.8 MPa |
| Elongation at break GB/T1040-2006 |
335.4 % | 345.6% | 346.5% |
| Shore hardness D GB/T2411-2008 |
62.8 | 62.4 | 60.4 |
| Impact strength GB/T1043-2008 |
74.6 KJ/m2 | 84.6 KJ/m2 | 89.54 KJ/m2 |
| Water absorption DIN EN ISO 62 |
＜0.01 % | ＜0.01 % | ＜0.01 % |
| Fire resistance UL94 |
HB | HB | HB |
| Mortar abrasion* TG-OG-D-006 /D |
7.7% | 5.9% | 4.9% |
| Raw materials | Celanese | Celanese 4158 | Celanese 4150 |
| Molecular weight | 7*10^6 g/mol | 8*10^6 g/mol | 9*10^6 g/mol |